| Mechanical analyzes were carried out on the recycled concrete samples obtained by preparing different mixtures of geopolymer powder, metakaolin, aggregates and alkali activator as sodium silicate (Na2SO3) and sodium hydroxide (NaOH) solution, which were formed by grinding the geopolymer concrete samples prepared with certain temperature and low curing times. In order to determine the contribution of metakaolin and ground geopolymer powders to the mechanical properties of geopolymer concrete, three different mixtures were prepared. In the three mixtures, ground geopolymer powder of 33.8%, 29.6% and 25.4% by volume, respectively, was used. In addition, metakaolin was used in the three mixtures at a rate of 0%, 4.2% and 8.4% by volume, respectively. The mixtures formed were kept in a curing environment at 45 and 75 ℃ for 8 hour, and mechanical properties (flexural and compressive … |
| Anahtar Kelimeler |
| Bildiri Türü | Tebliğ/Bildiri |
| Bildiri Alt Türü | Tam Metin Olarak Yayınlanan Tebliğ (Uluslararası Kongre/Sempozyum) |
| Bildiri Niteliği | Alanında Hakemli Uluslararası Kongre/Sempozyum |
| Bildiri Dili | İngilizce |
| Kongre Adı | The First International Cement Based Composites Congress-CEBACOM 2022 |
| Kongre Tarihi | 29-06-2022 / |
| Basıldığı Ülke | Türkiye |
| Basıldığı Şehir | Erzurum |