Effective utilization of silica fume and waste colemanite in eco-sustainable prepacked geopolymers
Yazarlar (6)
Doç. Dr. Haluk Görkem ALCAN Kafkas Üniversitesi, Türkiye
Prof. Dr. Ahmet Benli Bingöl Üniversitesi, Türkiye
Doç. Dr. Ali Öz Atatürk Üniversitesi, Türkiye
Doç. Dr. Barış BAYRAK Kafkas Üniversitesi, Türkiye
Doç. Dr. Gökhan Kaplan Atatürk Üniversitesi, Türkiye
Prof. Dr. Abdulkadir Cüneyt Aydın Atatürk Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | CONSTRUCTION AND BUILDING MATERIALS (Q1) | ||
| Dergi ISSN | 0950-0618 Dergi Bilgileri (2024) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | İngilizce | Basım Tarihi | 12-2024 |
| Cilt / Sayı / Sayfa | 457 / 0 / 139438–0 | DOI | 10.1016/j.conbuildmat.2024.139438 |
| Makale Linki | https://doi.org/10.1016/j.conbuildmat.2024.139438 | ||
| UAK Araştırma Alanları |
Yapı Malzemeleri
|
||
| Özet |
| In this work, the ternary prepacked aggregates geopolymer composites (PAGC) consisting of waste colemanite (WCM), silica fume (SF), and ground granulated blast furnace slag (GBFS) were created with the cement clinker aggregate (CCA). The performance and microstructure of PAGC mixtures were examined in relation to the impacts of WCM concentration and curing temperatures (ambient (23 °C), 50 °C, and 75 °C). WCM, SF, and GBFS were utilized in the production of PAGC as precursors. Sodium silicate (Na2SiO3) and sodium hydroxide (NaOH) were used as activators. Four PAGC mixes were created and cured at ambient (23 °C), 50 °C, and 75 °C for eight hours. Studies were done to determine the influence of WCM content and different curing temperature on the compressive strength, transport properties, flexural strength, sorptivity and dry unit weight properties of PAGC. The heat-resistant … |
| Anahtar Kelimeler |
| Prepacked aggregates geopolymer composites | Cement clinker aggregate | Waste colemanite | Curing temperature | High temperature |