Tribological and machining performance of tungsten carbide cutting tool material coated with different carbon nitride films
Yazarlar (5)
Fırat Dumlu
Dr. Öğr. Üyesi Tevfik Oğuzhan ERGÜDER Kafkas Üniversitesi, Türkiye
Dr. Öğr. Üyesi Gürkan Kaya Erzurum Teknik Üniversitesi, Türkiye
İlyas Hacısalihoğlu Türkiye
Prof. Dr. Fatih Yıldız Erzurum Teknik Üniversitesi, Türkiye
| Makale Türü | Özgün Makale (SSCI, AHCI, SCI, SCI-Exp dergilerinde yayınlanan tam makale) | ||
| Dergi Adı | INTERNATIONAL JOURNAL OF SURFACE SCIENCE AND ENGINEERING (Q4) | ||
| Dergi ISSN | 1749-785X Dergi Bilgileri (2022) | ||
| Dergi Tarandığı Indeksler | SCI-Expanded | ||
| Makale Dili | Türkçe | Basım Tarihi | 01-2022 |
| Cilt / Sayı / Sayfa | 16 / 3 / 258–275 | DOI | 10.1504/IJSURFSE.2022.125450 |
| Makale Linki | 10.1504/IJSURFSE.2022.125450 | ||
| UAK Araştırma Alanları |
Üretim Teknolojileri
Eklemeli İmalat
Triboloji
|
||
| Özet |
| In this study, the tribological properties of tungsten carbide (WC) cutting tools coated with AlTiCN and CrCN ceramic films and their machining performance were investigated in both CNC vertical machining centre and lathe. The coatings were applied on end milling tools, lathe inserts and 12 × 12 × 5 mm sized test samples by cathodic arc physical vapour deposition (CAPVD) method. The plastic injection mould steel workpiece was machined with high-speed dry cutting by CNC vertical machining centre and with coolant by CNC lathe to determine the cutting and wear performance of coated and uncoated tools. According to the results, it was determined that AlTiCN has higher microhardness and adhesion value and lower wear rate value than CrCN. It was also determined that the tools coated with AlTiCN thin film have superior properties in terms of both mass loss and flank wear width after machining processes. |
| Anahtar Kelimeler |
| AlTiCN | CrCN | CAPVD | carbon nitride film | cutting tool | wear | imachining | surface roughness |
BM Sürdürülebilir Kalkınma Amaçları
| Atıf Sayıları | |
| Web of Science | 3 |
| Google Scholar | 3 |