Synthesis and spectroscopic properties of nano-scale Y2O 3:Nd3+ phosphors
Yazarlar (4)
Prof. Dr. Gökhan BİLİR Kafkas Üniversitesi, Türkiye
G. Ozen
İstanbul Teknik Üniversitesi, Türkiye
J. Collins
Wheaton College, Amerika Birleşik Devletleri
B. Di Bartolo
Boston College, Amerika Birleşik Devletleri
Bildiri Türü Tebliğ/Bildiri Bildiri Dili İngilizce
Bildiri Alt Türü Tam Metin Olarak Yayınlanan Tebliğ (Uluslararası Kongre/Sempozyum)
Bildiri Niteliği Web of Science Kapsamındaki Kongre/Sempozyum
DOI Numarası 10.1149/05041.0001ecst
Kongre Adı Ecs Transactions
Kongre Tarihi /
Basıldığı Ülke Basıldığı Şehir
Bildiri Linki http://www.scopus.com/inward/record.url?eid=2-s2.0-84885794826&partnerID=MN8TOARS
UAK Araştırma Alanları
Fen Bilimleri ve Matematik
Özet
We report on the synthesis and spectroscopic characterization of Y 2O3:Nd3+ nano-powders synthesized by the thermal decomposition of yttrium alginate gels obtained by ionic gelation of yttrium salt solution and sodium alginate solution. The nano-powders were synthesized at 350, 400, 450 and 500 °C and annealed at 600, 800, 1000 and 1400°C. The cubic phase of the Y2O3 was confirmed, and the particle sizes range from 15 to 300 nm. For each sample we measured accurately the Nd + emission spectrum in a wide range of temperatures ranging from 35 to 300 K. We also measured the decay patterns of the excited Nd3+ ions following a pulsed excitation. These measurements were conducted in the same temperature range in order to fully characterize the samples examined. We have observed that these patterns vary considerably with the particle size, so that they may be considered signatures of these sizes.
Anahtar Kelimeler
BM Sürdürülebilir Kalkınma Amaçları
Atıf Sayıları
Web of Science 9
Scopus 12
Synthesis and spectroscopic properties of nano-scale Y2O 3:Nd3+ phosphors

Paylaş

İletişim
  • Kafkas Üniversitesi Rektörlüğü (36100) Merkez / KARS
  • unis@kafkas.edu.tr 4742251150 (474)225-1160
Sosyal Media
Talentsoft Yazılım Talent Yazılım
Tasarım ve Programlama #2025